Product weight: 25 kg/50 kg/100 kg
Product particle size: 15-45 µm
Text description:CoCrW is a cobalt-based alloy composed primarily of cobalt, chromium, and tungsten. It possesses excellent strength, hardness, and corrosion resistance, while also offering good aesthetics. Consequently, it has unique advantages in dental aesthetic restoration and is often utilised to fabricate the inner crown of all-porcelain crowns. Furthermore, it can also be used to create inlays and hyperinlays, which can precisely repair tooth defects, restore tooth shape and function, and aesthetically satisfy the patient’s requirements.
FM-CoCrW | 15-45 µm
| Chemical composition | |
| Element | wt% |
| Co | Bal. |
| Cr | 26-30 |
| W | 8-10 |
| Ni | ≤0.1 |
| N | ≤0.15 |
| O | ≤0.05 |
| Powder properties | ||
| Particle range | 15-45 μm | GB/T 19077 |
| Apparent density | ≥4.2 g/cm3 | GB/T 1479.1 |
| Tap density | ≥4.5 g/cm3 | GB/T 5162 |
| Hall speed | ≤25 s/50g | GB/T 1482 |
| Typical mechanical properties as printed | |
| Tensile strength | 1000±50 MPa |
| Yield strength | 800±50 MPa |
| Ductility | ≥30% |
Standard parking:
5 Kg/10 Kg/25 Kg/100 Kg
| Application | Dentistry, Medical |
|---|---|
| Technology | LPBF |