FM-H13 (ISO/EN:X40CrMoV5-1/JIS:SKD61/GB:4Cr5MoSiV1)

FM-H13 (ISO/EN:X40CrMoV5-1/JIS:SKD61/GB:4Cr5MoSiV1)

Product weight: 25 kg/50 kg/100 kg
Product particle size: 15-53 μm
Product description:H13 is a hot work die steel containing chromium, molybdenum, and manganese, offering high-temperature strength, wear resistance, and thermal fatigue performance. It is widely used in casting, hot forging, and hot pressing dies, adapting to high-temperature conditions.

 

Category:

Description

Tool Steel

 

FM-H13 | 15-53 µm

 

Chemical composition
Element wt%
Fe Bal.
Cr 4.75-5.5
Mo 1.1-1.75
V 0.8-1.2
Si 0.8-1.2
C 0.32-0.45
Mn 0.2-0.5
P ≤0.025
S ≤0.020

 

Powder proporties  
Particle range 15-53 μm GB/T 19077
Apparent density ≥4.3 g/cm3 GB/T 1479.1
Tap density ≥4.8 g/cm3 GB/T 5162
Hall speed ≤15 s/50g GB/T 1482

 

Typical mechanical proporties as pringted
Tensile strength 1800±50 MPa
Yield strength 1600±50 MPa
Ductility ≥8%

 

Standard parking:

5kg/10kg/25kg/100kg

 

 

Additional information

Application

Aerospace, Automotive, Mold
Technology

DED, EBM, LPBF, MIM